A cut above the rest
| GRADE | FEATURES | PROCESS | TDS |
|---|---|---|---|
| ORGALLOY LE 60 LM XV NATURAL | Plasticized polyamide alloy especially designed for tube extrusion. This natural grade dedicated to extrusion offers excellent barrier properties and chemical resistance to hydrocarbons, alcohols and solvents while exhibiting flexibility | Extrusion | - |
| ORGALLOY LT5050 T6L NATURAL | Polyamide alloy especially designed for tube extrusion. This natural grade dedicated to extrusion offers good barrier properties and chemical resistance to oils and HFC gas, a high thermal resistance and flexibility. | Extrusion | - |
| ORGALLOY RS 6000 (NATURAL) | Polyamide 6 alloy designed for injection molding. This natural grade offers an outstanding dimensional stability, chemical resistance to automotive fluids and is ideal for the realization of complex parts. | Injection | - |
| PLATAMID H 2513 | Copolyamide hot melt adhesive in pellets. Low–medium melt viscosity, fast re-crystallizing. Excellent adhesion to polar substrates. | Injection | - |
| RILSAMID AESN P202 CTL (BLACK) | Plasticized conductive PA12 grade for tube extrusion. Specially designed for conductive multi-layer fuel line applications. | Injection | - |
| RILSAMID AESN P302 TL (BLACK) | Plasticized PA12 grade for tube extrusion. Applications: air brake, motor vehicle tubing. Heat/light stabilized. | Extrusion | - |
| RILSAMID AESN T6L (BLACK) | Rigid PA12 grade for tube extrusion. Heat/light stabilized. Applications: automotive tubing. | Extrusion | - |
| RILSAMID AESNO MED | Rigid PA12 with high viscosity for medical tubing and catheters. Designed for minimally invasive devices. USP Class VI compliance possible. | Extrusion | - |
| RILSAMID AESNO P201 TL (NATURAL) | Natural plasticized PA12 grade for tube extrusion. Falls into PA12-PHLY category. Applications: automotive tubing. Heat/light stabilized. | Extrusion | - |
| RILSAMID AESNO P302 TL (NATURAL) | Natural plasticized PA12 grade for tube extrusion. Applications: air brake, motor vehicle tubing. | Extrusion | - |
| RILSAMID AESNO P40 TL | Natural plasticized PA12 grade for tube extrusion. Applications: air brake, motor vehicle tubing. Heat/light stabilized. | Extrusion | - |
| RILSAMID AMN T6LD (BLACK) | Black PA12 grade for injection molding. Heat/light stabilized. Applications: molded automotive parts. | Injection | - |
| RILSAMID ASR 13 (BLACK) | Carbon fiber reinforced PA12. Black grade for injection molding. Very high rigidity. Applications: structural automotive parts. | Injection | - |
| RILSAMID AZM 30 56827 TLD (GREEN) | Glass fiber reinforced PA12 grade for injection molding. Heat/light stabilized. Applications: automotive fittings, quick connectors. | Injection | - |
| RILSAMID AZM 30 632 TLD (GREY) | Glass fiber reinforced PA12 grade for injection molding. Heat/light stabilized. Applications: automotive fittings, quick connectors. | - | - |
| RILSAMID AZM 30 O TLD (NATURAL) | Glass fiber reinforced PA12 (GF30). Designed for injection molding. Applications: automotive fluid connectors. | Injection | - |
| RILSAMID AZM 30 T6LD (BLACK) | Glass fiber reinforced PA12 (GF30). Market standard for automotive fittings & heavy truck air brake connectors. | Injection | - |
| RILSAMID AZM 30 VERT 56827 TLD | Glass fiber reinforced PA12 grade, green variant. Designed for injection molding. Applications: automotive fluid connectors, heavy truck brake connectors. | - | - |
| RILSAMID AZM 50 T6LD (BLACK) | Glass fiber reinforced PA12 (GF50). Very rigid and tough. Applications: air brake connectors, automotive fittings. | Injection | - |
| RILSAN BECNO TL (NATURAL) | Bio-based PA11 natural grade for cable coating. >98% renewable carbon. Applications: wire and cable sheathing. | Injection & Extrusion | - |
| RILSAN BES BLACK PR | Bio-based PA11 black grade, plasticized for extrusion. Applications: fluid transportation, automotive tubing. | Extrusion | - |
| RILSAN BESN BLACK P40 TL | Bio-based PA11 black grade, plasticized for extrusion. Applications: fluid transport, air brake lines, fuel lines. | Extrusion | - |
| RILSAN BESN P024 TL (BLACK) | Bio-based PA11 impact-modified grade. Designed for low extractible fuel line applications. Applications: cooling circuits, gasoline lines. | Extrusion | - |
| RILSAN BESN P20 TL (BLACK) | Bio-based PA11 black grade, plasticized for extrusion. Applications: fluid transport, automotive tubing. | Injection & Extrusion | - |
| RILSAN BESN P210 TL (BLACK) | Bio-based PA11 black grade, plasticized for extrusion. 89% renewable carbon. Applications: fluid transport, automotive tubing. | Injection & Extrusion | - |
| RILSAN BESN P213 TL (BLACK) | Bio-based PA11 impact-modified grade. Improved hydrolysis resistance. Applications: cooling lines, SCR lines, heavy truck H2/gas lines. | Extrusion | - |
| RILSAN BESN TL (BLACK) | Bio-based PA11 black grade for extrusion. Applications: fluid transport, metal tubing sheathing. | Extrusion | - |
| RILSAN BESNO MED | Bio-based Polyamide 11 from renewable castor oil, specifically designed for medical extrusion applications, offering high purity, excellent chemical resistance, good flexibility, and reliable mechanical and thermo-mechanical properties | Injection | - |
| RILSAN BESNO P40 POL BB 1000K | Renewable PA11 with high flexibility, excellent impact resistance (no break in Charpy tests), good mechanical strength, low-temperature toughness, and suitability for extrusion applications | Extrusion | - |
| RILSAN BESNO P40 TL (NATURAL) | Plasticized bio-based PA11 developed for tube extrusion, offering excellent flexibility, high impact resistance, good chemical resistance, and stable mechanical performance | Extrusion | - |
| RILSAN BESNO TL (NATURAL) | Bio-based Polyamide 11 providing a balance of flexibility and mechanical strength, excellent resistance to chemicals, good barrier properties, and suitability for extrusion processes | Extrusion | - |
| RILSAN BESVO A MED | Medical-grade PA11 with high purity, low extractables, excellent chemical resistance, flexibility, and compliance with stringent medical application requirements | Extrusion | - |
| RILSAN BMN TLD (BLACK) | Injection-molding PA11 compound offering good stiffness, high mechanical strength, impact resistance, thermal stability, and light-stabilized performance | Injection | - |
| RILSAN BMNO | PA11, natural grade, 98% bio-based carbon content (ASTM D6866). No additives, food contact approved. Tensile modulus: 1280 MPa. Yield stress: 41 MPa. Shore D hardness: 68. Melting temperature: 189°C. Applications: Injected food parts. | Injection | - |
| RILSAN BMV 5 P20D (WHITE) | PA11 compound, bio-based (castor oil). Injection molding grade. Shrinkage: 1.5% (parallel/normal). Tensile modulus: 515 MPa. Yield stress: 32 MPa. Shore D hardness: 61. Melting temperature: 186°C. Applications: Outdoor balls, shuttlecock. | Injection | - |
| RILSAN BMW WITHE 5 P20D | PA11 compound, bio-based (castor oil). Injection molding grade. Shrinkage: 1.5% (parallel/normal). Tensile modulus: 515 MPa. Yield stress: 32 MPa. Shore D hardness: 61. Melting temperature: 186°C. Applications: Outdoor balls, shuttlecock. | Injection | - |
| RILSAN BSR30 R30 TLD (BLACK) | PA11, carbon fiber reinforced, 30% recycled (Virtucycle® program). Bio-based carbon content: 63%. Tensile modulus: 18500 MPa. Stress at break: 184 MPa. Shore D hardness: 80–83. Melting temperature: 184°C. Applications: Equipment. | Injection | - |
| RILSAN BUM 30 O (NATURAL) | PA11, glass bead reinforced, bio-based. WRAS drinking water approval. Tensile modulus: 1850 MPa. Stress at break: 31 MPa. Shore D hardness: 71. Melting temperature: 189°C. Applications: Drinking water. | Injection | - |
| RILSAN BZM 30 TL (BLACK) | PA11, fiberglass reinforced, bio-based. Tensile modulus: 6900 MPa. Stress at break: 110 MPa. Shore D hardness: 74. Melting temperature: 189°C. Applications: Quick connectors. | Injection | - |
| RILSAN BZM 8 OTL (NATURAL) | PA11, fiberglass reinforced, bio-based. Tensile modulus: 2300 MPa. Stress at break: 56 MPa. Shore D hardness: 73. Melting temperature: 189°C. Applications: Springs for quick connectors, outsoles. | Injection | - |
| RILSAN CLEAR G170 IN | Transparent amorphous polyamide. Heat stabilized. Tensile modulus: 2100 MPa. Yield stress: 76 MPa. Shore D hardness: 79. Glass transition temperature: 168°C. Applications: Sport equipment, health consumables, electronics. | Injection | - |
| RILSAN CLEAR G350 SC | High-performance transparent polyamide designed for injection molding, offering full transparency, flexibility, chemical resistance and durability for clear components such as eyewear frames and functional parts. | - | - |
| RILSAN CLEAR G830 SC | Bio-based transparent polyamide with high clarity and toughness, ideal for eco-design and high-clarity applications, combining transparency with durability and chemical resistance. | - | - |
| RILSAN FX0014 (BLACK) | TDS not publicly available online; typical Rilsan® PA11 based compound designed for enhanced mechanical and chemical performance in demanding molded parts (based on family description of Rilsan® PA11 performance). | Extrusion | - |
| RILSAN G350 (CLEAR) | Transparent polyamide grade with design freedom, full transparency, flexibility and good chemical resistance for injection molding applications. | Injection | - |
| RILSAN G820 RNEW (CLEAR) | Transparent copolyamide, bio-based (45%). Tensile modulus: 1680 MPa. Yield stress: 64 MPa. Shore D hardness: 74. Glass transition temperature: 145°C. Applications: Eyewear frames, optics, smartphone frames. | Extrusion | - |
| RILSAN G820 RNEW (CLEAR) SC | Bio-based transparent polyamide with good transparency, chemical resistance and processing stability, suitable for clear injection molded parts. | Extrusion | - |
| RILSAN G850 RNEW (CLEAR) | Transparent copolyamide, bio-based (45%). Tensile modulus: 1680 MPa. Yield stress: 64 MPa. Shore D hardness: 74. Glass transition temperature: 145°C. Applications: Eyewear frames, optics, smartphone frames. | Injection | - |
| RILSAN HT CESV BLACK P010 HP TL | Polyphthalamide compound, bio-based (48%). Flexible, high thermal and chemical resistance. Tensile modulus: 1050 MPa. Yield stress: 34 MPa. Shore D hardness: 66. Melting temperature: 260°C. Applications: Automotive fluid transfer lines. | Extrusion | - |
| RILSAN HT CESV P010 TL (BLACK) | Flexible polyphthalamide, bio-based (48%). Tensile modulus: 1015 MPa. Yield stress: 30 MPa. Shore D hardness: 66. Melting temperature: 260°C. Applications: Automotive tubing, hydraulic and pneumatic lines. | Extrusion | - |
| RILSAN HT CSR 13 | Fiber reinforced polyphthalamide, bio-based (52%). Conductive grade. Tensile modulus: 7600 MPa. Stress at break: 151 MPa. Shore D hardness: 66. Melting temperature: 255°C. Applications: Conductive automotive quick connectors. | Injection | - |
| RILSAN HT CZM 30 TLD (BLACK) | TDS not publicly available online; reinforced high-temperature PA11 alloy designed for engineered parts needing mechanical strength and thermal performance (Arkema PA11 range known for durability). | Injection | - |
| RILSAN MB 3000 (NATURAL) | PA11, halogen-free flame retardant. Melt flow 95 cm³/10 min. Tensile modulus 1830 MPa, yield stress 45 MPa, Shore D 69, melting temp 189°C. Burning class V-0, oxygen index 33%. Density 1090 kg/m³. Applications: wire/cable sheathing, rollers. | Injection | - |
| RILSAN MG350 CLEAR | TDS not publicly available online separately; expected to share typical Rilsan® Clear characteristics — transparency, design flexibility, and chemical resistance for molded components. | - | - |
| RILSAN TESN BLACK P413TL | TDS not publicly available online; PA11 resin likely plasticized for improved flexibility and mechanical resilience in injection molded components (general PA11 family behavior). | - | - |
| RILSAN TESN BLACK P513 TL | TDS not publicly available online; similar to P413TL with tailored plasticization for enhanced flexibility and toughness | - | - |
| RILSAN TESNO P413 TL | TDS not publicly available online; PA11 resin plasticized for resilience and chemical resistance in molded applications. | - | - |
| RILSAN TIEFLEX R073 T6L (BLACK) | TDS not publicly available online; PA11-based flexible tie layer elastomer grade (Arkema product family information suggests tie layer applications). | Extrusion | - |
| RILSAN TIEFLEX R463 | Polyamide alloy, partially bio-based. Melt flow 8 cm³/10 min. Tensile modulus 500 MPa dry, 330 MPa conditioned. Yield stress 28 MPa, yield strain 50%. Melting temp 214°C. Density 1.08 g/cm³. Applications: heavy truck air brake lines. | Extrusion | - |
| RILSAN TIEFLEX R463 BLACK | Polyamide alloy pellet partially bio-based designed for multilayer air brake applications as structural tie layer in tubing, offering flexibility and renewable content. | Extrusion | - |
| RILSAN TIEFLEX R473 NATURAL TL | Flexible tie layer alloy, partially bio-based. Melt flow 5.4 cm³/10 min. Stress at 50% strain 28 MPa. Strain at break >50%. Charpy notched impact 100 kJ/m² at +23°C, 11 kJ/m² at -30°C. Melting temp 215°C. Density 1100 kg/m³. Applications: air brake tubing. | Extrusion | - |